7075 aluminum rod
Brand: Alcoa Caesars Standard: ASTM AMS QQ
7075 is a cold-treated forging alloy with high strength, far better than mild steel. 7075 is one of the most powerful alloys commercially available. General corrosion resistance, good mechanical properties and anode reaction. The small grains make the deep drilling performance better, the tool wear resistance is enhanced, and the thread rolling is more different.
Tensile strength 524Mpa 0.2% Yield strength 455Mpa elongation 11%
Introduction to 7075 Aluminum Rod
7075 aluminum rod spot specification: diameter 10-70 (mm)
Silicon Si: 0.40 Copper Cu: 1.2～2.0 Magnesium Mg: 2.1～2.9 Zinc Zn: 5.1～6.1
Manganese Mn: ≤0.30 Titanium Ti: ≤0.20 Chromium Cr: 0.18～0.28
Iron Fe: 0.50
Note: Single: ≤0.05; Total: ≤0.15
Aluminum Al: margin
The material composition and process are strictly controlled to ensure that the material composition and mechanical properties of each batch meet or exceed the national standard.
7075 aluminum rod processing characteristics
7075 aluminum is called ultra-high-strength aluminum alloy. The yield strength of the alloy is close to the tensile strength, the yield ratio is high, and the specific strength is also high, but the plasticity and high temperature strength are low. Parts, alloys are easy to process, have good corrosion resistance and high toughness. The alloy is widely used in aviation and aerospace fields, and has become one of the most important structural materials in this field.
Mechanical and physical properties of 7075 aluminum rod
Tensile strength: 524Mpa
0.2% yield strength 455Mpa
Elastic modulus: E/Gpa:71.
7075 aluminum rod product features
1. High-strength heat-treatable alloy.
2. Good mechanical properties.
3. Good usability.
4. Easy to process and good wear resistance.
5. Good corrosion resistance and oxidation resistance.